tratamiento termico 1. temple de las principales calidades
Anuncio
Schmolz + Bickenbach Mexico, S.A de C.V. 16PRESH3 TRATAMIENTO TERMICO 1. TEMPLE DE LAS PRINCIPALES CALIDADES CALIDAD TEMPERATURA ENFRIAMIENTO DUREZA P THYRODUR 1730 820 - 850 °C 2 35 HRc 1 THYRODUR 1730 820 - 850 °C 5 58 HRc 2 THYRODUR 2080 930 - 960 °C 1 64 HRc 1 THYRODUR 2080 950 - 980 °C 2 64 HRc 2 THYRODUR 2363 930 - 970 °C 1,2,3 63 HRc THYRODUR 2379 1000 - 1050 °C 1,2,3 63 HRc 1 THYRODUR 2379 1050 - 1080 °C 1,2,3 61 HRc 2 THYRODUR 2436 950 - 980 °C 1,2,3 64 HRc THYRODUR 2510 780 - 820 °C 2,4 64 HRc THYRODUR 2550 870 - 900 °C 2,4 60 HRc THYRODUR 2767 840 - 870 °C 1,2,3 56 HRc THYRODUR 2990 870 - 900 °C 2,4 63 HRc THYROTHERM 2344 1020 - 1050 °C 1,2,3 54 HRc THYROTHERM 2365 1020 - 1050 °C 1,2,3 52 HRc THYROTHERM 2367 1030 - 1080 °C 1,2,3 57 HRc THYROTHERM 2714 830 - 870 °C 2 58 HRc 1 THYROTHERM 2714 860 - 900 °C 1 56 HRc 2 THYROTHERM 2885 1000 - 1050 °C 1,2,3 54 HRc THYROTHERM 2999 1050 - 1100 °C 2,3 57 HRc THYRAPID 3243 1190 - 1230 °C 1,2,3 64/67 HRc THYRAPID 3247 1160 - 1190 °C 1,2,3 66/69 HRc THYRAPID 3343 1180 - 1220 °C 1,2,3 64/66 HRc TSP4 1050 - 1230 °C 1,2,3 58/65 HRc THYROPLAST 2083 1000 - 1050 °C 2,3 56 HRc THYROPLAST 2316 1020 - 1050 °C 2,3 49 HRc 1 1 = AIRE 2 = ACEITE 3 = BAÑO DE SAL A 500 - 550 °C 4 = BAÑO DE SAL A 180 - 220 °C 5 = AGUA p = existen diferentes procesos de temple * RECORDAR QUE EL TIPO DE ENFRIAMIENTO DEPENDE DE LA CONFIGURACION DE LAS PIEZAS Calidad tratamiento termico al vacio Norma DIN- Templabilidad (5bar N 2) HRc THYRODUR 2721 THYRODUR 2767 THYRODUR 2510 THYRODUR 2550 THYRODUR 2842 THYRODUR 2363 THYRODUR 2080 THYRODUR 2436 THYRODUR 2379 50NiCr13 X45NiCrMo4 100MnCrW4 60WCrV7 90MnCrV8 X100CrMoV5-1 X210Cr12 X210CrW12 X155CrVMo12-1 59 56 64 60 63 63 64 64 63 THYROTHERM 2714 THYROTHERM 2343 THYROTHERM 2344 THYROTHERM 2365 THYROTHERM 2885 56NiCrMoV7 X38CrMoV5-1 X40CrMoV5-1 X32CrMoV3-3 X32CrMoCoV3-3-3 56 54 54 50 52 THYROPLAST 2083 THYROPLAST 2316 X42Cr13 X36CrMo17 56 49 0 20 40 60 80 100 120 140 160 180 200 Medida en mm